Datasheet: Haynes˘ 214

Haynes˘ 214

Haynes 214 is a Nickel-Chromium-Aluminium-Iron alloy which is principally intended for use at temperatures of 955 °C (1750 °F) and above. It exhibits resistance to oxidation that far exceeds virtually all conventional heat resistant wrought alloys at these temperatures, which is attributable to the forming of an Al2O3-type protective oxide scale, which forms in preference to Chromium Oxide scales at such high temperatures. Best suited for high temperature, low stress environments, Haynes 214 is used in the aerospace, automotive, industrial heating and medical industries, as well as for land-based gas turbines.

Haynes 214 is also known as Cabot 214 and Hastelloy 214.

Available in all profile options

Haynes˘ 214 - Alloy Wire International 1

Key Features

Haynes 214 offers the following key features:

Resistance to oxidation that far exceeds most heat resistant alloys at temperatures of 955 ºC (1750 ºF) and above.
High temperature static applications. **

Typical Applications

Haynes 214 is known to be suitable for the following applications:

Mesh belts.
Trays and fixtures for the firing of pottery and china, and the heat treatment of electronic devices and technical grade ceramics.


Designations

W.NR 2.4646
UNS N07214
AWS 061

Specifications

Chemical Composition

The chemical composition of Haynes 214 is indicated in the table below:

ElementMin %Max %
Al4.105.00
B0.004
C0.05
Nb/Cb0.15
Co2.00
Cr15.0017.00
Fe2.004.00
Mg0.01
Mn0.50
Mo0.50
Nibal
P0.015
S0.015
Si0.20
Ti0.50
W0.50
Y0.0030.04
Zr0.02

Alloy Details

Haynes 214 density, melting point, coefficient of expansion, and modulus of elasticity is indicated in the table below:

DensityMelting PointCoefficient of ExpansionModulus of RigidityModulus of Elasticity
8.05 g/cm³1400 °C13.3 μm/m °C (20 – 100 °C)84 kN/mm²217 kN/mm²
0.291 lb/in³2550 °F7.4 x 10-6 in/in °F (70 – 212 °F)12183 ksi31474 ksi

Heat treatment of finished parts

The typical heat treatment of Haynes 214:

Condition as supplied by AWITypeTemperatureTimeCooling
Annealed or Spring TemperStress Relieve400 – 450 °C (750 – 840 °F)2 HrAir

Properties

The typical mechanical properties of Haynes 214:

Annealed
Approx. tensile strength<1200 N/mm²<174 ksi
Approx. operating temperature depending on load** and environment-200 to +1100 °C-330 to +2010 °F
Spring Temper
Approx. tensile strength1300 – 1700 N/mm²189 – 247 ksi
Approx. operating temperature depending on load** and environment-200 to +1100 °C-330 to +2010 °F